Preparation and characterization of an ultrafine cobalt powder with lower sintering temperature

Abstract At present, domestic diamond tools and cobalt powder are produced. Ammonium bicarbonate is used as a precipitant to prepare ultrafine cobalt powder by precipitant-thermal decomposition-reduction process. The effects of temperature and pH on the process parameters in the process of precipitant were studied, and ultrafine cobalt powder with Fsss particle size of 0.5~1μm was prepared. The morphology of ultrafine cobalt powder was observed by SEM. 40mmX8mmX3.2 samples were prepared by hot pressing sintering, and the hardness and flexural strength of the samples were characterized. Compared with the traditional oxalic acid precipitation reduction to produce cobalt powder, the cobalt powder of the process equipment has a fine crystal spherical shape and higher activity. The hot-pressed sintered sample of such ultrafine cobalt powder can obtain higher hardness at a lower temperature, and exhibits good stability in bending strength at different temperature ranges, and reduces production cost.


Diamond and Abrasives Engineering, 2009, Issue 3

Heavily Hot-Dip Galvanized Wire

Heavily Hot dipped Galvanized Wire

Zinc: 200-350g/m2

T/S: 380-500Mpa

Packing: plastic film inside, hessian woven bag or nylon woven outside

Shen Zhou City Hongda Hardware Products Co.,Ltd is a family owned company, founded in 1998, loacated at Tang feng industry zone, Shen Zhou. It has covered an area of 20 hectares, with a total asset of 20 million and more than 300 people with 80 engineering technicians, a 5-person research group, and a service group dedicated to provide the best solutions.

Heavily Hot-Dip Galvanized Wire,Heavily Galvanized Wire,Heavily Hot Dipped Wire,Woven Mesh Gabions

Shenzhou City Hongda Hardware Products Co.,Ltd , https://www.hdpvcwire.com