Hardware encyclopedia | What is the difference between quenching and heat treatment of stud manufacturers?
The heat treatment process generally includes three processes of heating, heat preservation and cooling, and sometimes only two processes of heating and cooling. These processes are connected to each other and cannot be interrupted.
Heating is one of the important processes of heat treatment. There are many heating methods for metal heat treatment. In the early days, charcoal and coal were used as heat sources, and liquid and gaseous fuels were applied nearby. Electrical applications make heating easy to control and environmentally friendly. These heat sources can be used for direct heating, or by indirect heating of molten salts or metals, or floating particles.
When the stud metal is heated, the workpiece is exposed to the air, and oxidation and decarburization (ie, the carbon content on the surface of the steel part) often occur, which has a detrimental effect on the surface properties of the parts after heat treatment. Thus, the metal should generally be heated in a controlled or protective atmosphere, in a molten salt and in a vacuum, or protected by a coating or packaging process.
Heating temperature is one of the important process parameters of the heat treatment process. The selection and control of the heating temperature by the stud manufacturers is the main problem to ensure the quality of the heat treatment.
The heating temperature varies depending on the metal material to be treated and the purpose of the heat treatment, but is generally heated above the phase transition temperature to obtain a high temperature structure. In addition, the transformation takes a certain time, so when the surface of the metal workpiece reaches the required heating temperature, it must be kept at this temperature for a certain period of time, so that the internal and external temperatures are uniform, and the microstructure is completely transformed. This period of time is called the holding time. When high-energy density heating and surface heat treatment are used, the heating rate is extremely fast, and generally there is no holding time, and the heat treatment time of the chemical heat treatment tends to be long.
Cooling is also an indispensable step in the heat treatment process. The cooling method varies from process to process, mainly to control the cooling rate. Generally, the annealing rate is the slowest, the normalizing cooling rate is faster, and the quenching cooling rate is faster. However, there are different requirements depending on the type of steel. For example, an empty hard steel can be hardened at the same cooling rate as a normal fire.
Stud quenching and tempering treatment is quenching + high temperature tempering = double heat treatment of quenching and high temperature tempering, the purpose of which is to make the workpiece have good comprehensive mechanical properties.
Heat treatment refers to a metal thermal processing process in which materials are heated, held, and cooled in a solid state to obtain desired structure and properties.
Quenching and tempering treatment: The heat treatment method of high temperature tempering after quenching is called quenching and tempering treatment. High temperature tempering refers to tempering between 500-650 °C. The quenching and tempering of the stud manufacturers can greatly adjust the properties and materials of the steel, and its strength, plasticity and toughness are good, and it has good comprehensive mechanical properties. After quenching and tempering treatment, tempered sorbite is obtained.
Tempered sorbite is formed when martensite is tempered and can be distinguished by magnifying 600 times or more under an optical microscope microscope. It is a carbide (including cementite) distributed in the ferrite matrix. The composite structure of the pellets. It is also a tempering structure of martensite, a mixture of ferrite and granular carbide. At this time, the ferrite has substantially no carbon supersaturation, and the carbide is also a stable carbide. At room temperature is a balanced organization.
With the increase in the application of electric power fittings, the development of electric power fittings will be more rapid, and because of the wide application of electric power fittings, its quality problems will be one of the issues we attach importance to. Therefore, we should consider some of the high-level problems that we have to undertake in the process. Fan-shaped aluminum wire, power cable and excessive connection of copper ends of electrical equipment, such products also play a vital role in the power fittings. 
Editor in charge: Hu Na
Diamond Electroplating Abrasive Belts are nickel-plated as a binder and are made from diamond powder. Diamond electroplated abrasive belts consist of a backing material, a metal base, and an array of diamond coatings. The backing material and the flexible metal substrate are bonded to form a ring-shaped super-hard coated abrasive. As a result of special stainless steel, double-layer backing and selected high-quality diamonds, our Flexible Diamond Belt a very fast chip, the chip minimum, very long lifetime to achieve good tempering results, it can be done all the games. Our flexible diamond belt is widely used in wet and polishing applications in the aerospace, ceramics, glass, paper and stone industries. The advantages are consistency, increased productivity, reduced downtime and wear costs. The average life expectancy of our diamond abrasives is 1,000 times longer than that of conventional abrasives compared to conventional abrasives. Most sizes are available for many applications on hand-held or robotic machines and all sizes are available or can be made as a fit-to-hand, cross belt and robotic machine.
1.1 Compared with ordinary abrasive belt
Diamond electroplated abrasive sanding belt has the characteristics of hardness of superhard material and the softness of the coated abrasive. The working layers is arranged, making the gap between the small units of the working layer larger, there will be a bigger chip removing space, it is good for cooling, improving the processing quality, flexible of sanding belt and chip removal capacity. It is low noise and little dust when using.
1.2 Compared with Diamond Grinding Wheels
Diamond Grinding Wheel is a rigid abrasive tool. In the grinding process, there are not good self-sharpening and easy to chip . Especially when automotive wind safety glass and other material need to be processed as curved surface of hard and brittle materials, if use diamond electroplated abrasive sanding belt can improve the grinding feed rate and working efficiency. And effectively solve the problem of glass chipping and maintain the original shape of the surface very good.
1.3 Compared with diamond resin belt
Diamond resin belt has resin bonded, also has double advantages of softness of a traditional coated abrasive and high hardness of the diamond. But when grinding, the heat will be accumulated in the diamond, it the heat will not be derived immediately, the temperature will be increased immediately, resulting the bond agent melting, the diamond will fall, and the service life is short. So diamond resin belt must grind by adding water to cooling, and the cost-effective of that is worse than diamond electroplated abrasive sanding belt.
Application of Diamond Electroplated Abrasive Sanding Belt
Diamond electroplated abrasive sanding belt can be widely used in stone, glass, ceramics, monocrystalline silicon, polycrystalline silicon, synthetic materials, hard alloy, aluminum alloy and other hard and brittle material complex surface grinding processing.
Flexible Diamond Abrasive Sanding Belts
flexible diamond abrasive belts,Diamond Grit Sanding Belts,Diamond Abrasive Grit Belt,Diamond Abrasive Belts Glass,Diamond Grit Sanding Belt,Flexible Diamond Abrasive Belts,Flexible Diamond Belt
Hans Superabrasive Material Co., Ltd. , https://www.hansuperabrasive.com